Increase in interfacial adhesion and electrochemical charge storage capacity of polypyrrole on au electrodes using polyethyleneimine

ABSTRACT High-performance devices based on conducting polymers (CPs) require the fabrication of a thick CP-coated electrode with high stability. Herein, we propose a method for enhancing the

interfacial adhesion strength between a gold electrode and an electropolymerized polypyrrole (pPy) layer by introducing a polyethyleneimine (PEI) layer. Although this insulating layer

hinders the initial growth of the pPy layer on the Au surface, it improves the adhesion by up to 250%. Therefore, a thick layer of pPy can be fabricated without delamination during drying.

X-ray photoelectron spectroscopy shows that the PEI layer interacts with the Au surface via polar/ionic groups and van der Waals interactions. Scanning electron microscopy reveals that the

cohesion of the pPy layer is stronger than the interfacial adhesion between the PEI layer and the pPy layer. Importantly, the electroactivities of pPy and its dopant are unaffected by the

PEI layer, and the electrochemical storage capacity of the pPy layers on the PEI-coated Au electrodes increases with thickness, reaching ~530 mC/cm2. Negative potential sweep is detrimental

to pPy layer adhesion: pPy layers on a bare Au electrode peel off instantly as the potential is swept from 0.2 to −0.7 V, and most of the charge stored in the layer becomes inaccessible. In

contrast, pPy layers deposited on PEI coated Au electrode are mechanically stable and majority of the charge can be accessed, demonstrating that this method is also effective for enhancing

electrochemical stability. Our simple approach can find utility in various applications involving CP-coated electrodes, where thickness-dependent performance must be improved without loss of

stability. SIMILAR CONTENT BEING VIEWED BY OTHERS ENHANCED ADHESION OF PEDOT:PSS TO SUBSTRATES USING POLYDOPAMINE AS A PRIMER Article Open access 24 October 2023 ROBUST METAL ION-CHELATED

POLYMER INTERFACIAL LAYER FOR ULTRAFLEXIBLE NON-FULLERENE ORGANIC SOLAR CELLS Article Open access 09 September 2020 TRI-SYSTEM INTEGRATION IN METAL-OXIDE NANOCOMPOSITES VIA IN-SITU

SOLUTION-PROCESSED METHOD FOR ULTRATHIN FLEXIBLE TRANSPARENT ELECTRODES Article Open access 07 March 2024 INTRODUCTION Conducting polymers (CPs) such as polypyrrole (pPy) are attracting

considerable interest because their redox activity, conductivity, and biocompatibility are useful for various applications, including electrochemical energy storage devices, actuators, and

neural interfaces. To fabricate high-performance CP electrodes, it is often desirable to deposit a thick CP layer on the electrode because its performance is highly dependent on this layer’s

thickness; for instance, the areal energy/power densities (Wh/cm2, W/cm2) or actuating force of a CP electrode are proportional to its thickness1,2. However, it is challenging to develop a

thick CP layer because of the low interfacial adhesion strength between the CP layer and the underlying electrode. Accordingly, the CP layer can easily peel off from the electrode during

fabrication and operation. One strategy to overcome this delamination issue is to roughen the electrode surface by either etching or electroplating its surface3. Although mechanical

interlocking between the overlaying CP layer and the rough metal surface has been shown to improve interfacial adhesion3,4, the CP layers were only a few microns thick. Additionally, the

etching process could expose an electrochemically reactive underlying layer (such as Ti), making the CP-coated electrode unstable during long-term application. An alternative strategy

involves the formation of covalent bonds between the electrode surface and the pPy layer using modified pyrrole monomers5,6. However, this method requires additional effort to synthesize the

monomers, and some covalent bonds such as Au surface and thiolated pyrrole cannot be used for electrochemical cycling of the CP layer due to their instability6. A recent study showed that

the use of a bioinspired adhesive molecule, dopamine, as a dopant for pPy resulted in good interfacial adhesion7. However, this method cannot be extended to other functional dopants. To

address the delamination issue, we have developed a new strategy that utilizes an adhesion-enhancing layer between the CP layer and the metal electrode. Herein, we examined a

high-molecular-weight branched polyethyleneimine (PEI) as a candidate material for such an adhesion-enhancing layer because of its good adhesion to metals8, charged polyelectrolytes9, and

cells10 via van der Waals or ionic/polar group interactions. Moreover, its chain flexibility and large free volume are suitable for accommodating an incipient electropolymerized CP layer. In

this study, we used pPy doped with a redox-active molecule, namely, indigo carmine (IC), as a model CP layer, because it showed good electrochemical performance for energy storage

applications and the thickness of the pPy layer was limited to the submicron scale11. Our approach improved significantly the adhesion between the pPy layer and the electrode surface.

Importantly, the physical characteristics (e.g., morphology, thickness, and charge dependence) and the electroactivity of the pPy layer were not affected by the presence of the PEI layer.

Therefore, this simple strategy allowed us to develop thicker pPy layers without compromising their performances. We validated the effectiveness of our method by demonstrating pPy layers

with enhanced areal capacities and electrochemical performances. MATERIALS AND METHODS PREPARATION OF ELECTRODE SURFACE Single crystal Si (100) wafers with a 100-nm-thick layer of SiO2 were

used as substrates for the experiments. An e-beam evaporator (SRN 200, Sorona) was used to prepare the Au working electrode by evaporating the metal layers of Ti (10 nm) and Au (50 nm) on

one side of the Si wafer. All the Au electrode surfaces were cleaned sequentially under sonication with acetone, ethanol, and deionized (DI) water for 5 min. O2 plasma treatment (Plasma

Cleaner, PDG-32G, Harrick Plasma) was performed for 2 min on the Au electrode. For PEI (MW = 750,000 g mol−1, Sigma Aldrich) adsorption, the electrode was immersed in a 0.5 mg/mL PEI

solution for 24 h. For the preparation of thick polymer-coated Au electrodes, a plasma-treated Au electrode was coated with a layer-by-layer assembly of a positively charged polymer (linear

polyethyleneimine, LPEI) and a negatively charged polymer (poly(acrylic acid), PAA (MW = 250,000 g mol−1)9. The layer by layer assembly process is shown in Fig. S1. A plasma-treated Au

electrode was first immersed in solution of LPEI for 15 min, followed by immersion of the electrode three times in DI water for 3, 1, and 1 min to remove excess LPEI that is loosely bound to

the surface. Then, the electrode was immersed in a solution of poly(acrylic acid) (PAA) and subsequent washing as mentioned above. This deposition process was repeated 5 times to obtain a

thick polymer coating on the Au surface. CHARACTERIZATION OF ELECTRODE SURFACE The amount of PEI adsorption on the gold surface was measured using a quartz crystal microbalance (QCM)

(QCA-922, Seiko EG&G). The PEI layer was adsorbed onto one side of Au quartz (QA-A9M Au), which was assembled into dip cells (QA-CL3). The frequency was measured and compared under a

constant relative humidity of 30 % and temperature of 23 °C. The QCM results for PEI-O2 were tested four times, while those of PEI Au were tested three times, after which the mean and

standard deviations were calculated. X-ray photoelectron spectroscopy (XPS) measurements were carried out on the Au surfaces within an area of 100 μm × 100 μm (Quantera SXM, ULVAC-PHI). The

XPS spectra of C 1 s, N 1 s, and Au 4 f regions were fitted using a Gaussian function after background subtraction. The surface morphologies of the species absorbed on the Au surface were

characterized using atomic force microscopy (AFM, NX20, Park Systems). ELECTRODEPOSITION AND CHARACTERIZATION OF PPY LAYER A thin film of pPy was electrodeposited onto the surface-modified

Au-Si wafer (1.5 cm × 0.5 cm area) by applying a constant potential of 0.70 V (vs. Ag/AgCl) in an aqueous solution containing 200 mM pyrrole and 25 mM indigo carmine (IC, Sigma Aldrich)11.

The thickness of the pPy layer was determined by controlling the charge per unit area. All thickness profiles and roughness characteristics of the pPy samples were obtained using a Dektak

150 instrument. Cyclic voltammetry (CV) was performed in 0.2 M HCl solutions at various potential windows and scan rates. After electrodeposition of the pPy layer on the Au electrode, the

electrode was rinsed with DI water and dried under a fixed relative humidity (30 %) and temperature (23 °C). The surface morphologies of the delaminated pPy layer and the Au surfaces after

delamination were observed by field emission scanning electron microscopy (FE-SEM) (S-4800, Hitachi High-Technology). RESULTS AND DISCUSSION Figure 1 shows our strategy for enhancing the

adhesion between the electrodeposited pPy layer and the Au electrode. First, the electrode surface is treated with O2 plasma to produce polar functional groups (e.g., carbonyl) on the

surface12. Second, a PEI layer (orange line) physisorbs onto the plasma-treated electrode via electrostatic interactions involving the positively charged groups of PEI and the polar groups

on the electrode surface. After application of the PEI layer, pPy (black line) is then electrodeposited onto this surface (PEI-O2 Au). Figure 1(b) shows the digital images of the PEI-O2 Au

surface before and after the pPy electrodeposition. The PEI-O2 Au surface was indistinguishable from the bare Au surface to the naked eye; by contrast, after the electrodeposition, the

surface was covered with a black coating of pPy. In order to investigate the interactions between the PEI and the O2 plasma-treated Au surface, XPS was performed on the Au surface before and

after the coating with the PEI layer. After coating, new peaks assigned to PEI appeared: N 1 s peaks at 401.5 and 399.9 eV, corresponding to N+ and NH/NH2 species, respectively (Fig. 2(a)),

and a C–N peak at 286.9 eV (Fig. 2(b)). Additionally, the C = O and Au 4 f peaks shifted by 1.0 and −0.15 eV with respect to their original position in the spectrum of the uncoated Au

surface, respectively (Fig. 2(c,d)). The slight negative shift of the Au 4 f peaks indicated that the gold surface was reduced by the non-protonated amino groups of PEI13. The positive shift

of the C = O peak after PEI adsorption indicates the interactions between C = O and the positively charged amino groups of PEI14,15. These results show that the PEI layer interacts with

both the carbonyl groups present on the treated surface and the Au metal surface. We quantified the amount of PEI layer adsorbed onto the O2 plasma-treated Au electrode using QCM. The amount

was 0.64 ± 0.252 μg/cm2, indicating that a PEI layer of 6.4 nm thickness adhered to the Au surface, assuming its density to be 1.03 g/cm3 16. This thickness is much greater than that of a

PEI monolayer coating (~0.6 nm)14, which suggests aggregation of the PEI layer. Scanning electron microscopy (SEM) confirmed that the O2 plasma-treated Au electrode was covered with a

non-uniform coating of PEI. As shown in Fig. 3(a), dark irregular patches of PEI covered a portion of the electrode surface after the adsorption of PEI; this region has multiple PEI dots on

the surface, although most of the area appears similar to the uncoated Au surface (Fig. 3(b,c)). Therefore, a small fraction of the surface appeared to be coated with PEI when visualized by

SEM, and the remaining surface was relatively unaffected. After plasma treatment on Au surface, gold oxide is formed, carbon contamination is removed, and polar groups (e.g. CO) appear14,15.

It has been reported that gold oxide and the sites of polar groups are non-uniform and discontinuous on the surface17. The affinity of PEI to different surface sites would be different, and

therefore, PEI adsorption should be non-homogenous. AFM revealed that the roughness of this remaining surface was slightly lower than that of the uncoated Au surface (Table S1 and Figure

3(d–f)). This result suggests that this region was also affected by the PEI since the application of a PEI coating on a substrate generally produces smooth surfaces14. A pPy layer was

electrodeposited on the Au surfaces by applying a constant oxidative potential. The chronoamperograms of pPy electropolymerization shown in Fig. 4(a) reveal the effect of surface conditions

on the layer growth. When a bare Au or O2 plasma-treated Au electrode was used, the chronoamperometric curves showed a steep increase in the initial current, demonstrating that pPy deposited

rapidly on these surfaces. By contrast, when the PEI-O2 Au electrode was used, the chronoamperometric curves exhibited a gradual increase in the initial current, demonstrating that the

growth of pPy is hindered by the electrically insulating PEI layer on the surface. Given that the typical electrodeposition process takes up to ~2000 s, the PEI layer on the Au surface would

undergo local rearrangement of its repeat unit and become entangled with the extended chains of pPy via site/polymer diffusion18. The PEI layer impedes the initial growth of the pPy layer,

so the deposition time required for fabricating a pPy layer on PEI-coated Au is longer than that required for a pPy layer on a bare electrode, given that the thicknesses are the same.

However, the relationship between the chronometric charge and the thickness or the topology was unaffected by the presence of the PEI layer (Fig. 4(b)). The electrical conductivity of the

pPy films was measured using the four-point probe method. Regardless of the presence of the PEI coating, the conductivity of the pPy films on Au electrodes was similar (~0.2 S/cm). This

conductivity is within the range of values observed for pPy films (0.001 to 100 S/cm)19,20. Following pPy electropolymerization, the wet pPy layers were rinsed and dried in air. As water

evaporates from the pPy layer, it shrinks and delaminates when its thickness is larger than a certain value (delamination thickness) for a given surface treatment and environment (e.g.,

humidity and temperature; Fig. 5(a,b)). Generally, the total strain energy released (Gc) during the delamination of a layer from a rigid substrate quantifies the interfacial adhesion and it

is proportional to the delamination thickness21. Therefore, the delamination thickness represents a measure of the relative interfacial adhesion strength. Figure 5(c) shows that the

delamination thickness of the pPy layer on the bare Au electrode was 9 µm, but was ~23 µm (i.e., 250% higher) on the PEI-O2 Au electrode. Clearly, these results demonstrate that our proposed

surface treatment method does indeed enhance the interfacial adhesion. Additionally, the bonding between the pPy layer and the PEI-O2 Au electrode was stronger than that with the PEI-coated

Au without O2 treatment, confirming that polar groups on the O2-treated Au contribute to the enhanced interfacial adhesion. The positively charged pPy backbones may be attracted directly to

the surface polar groups (e.g. C = O) of the O2-treated Au surface even though the surface is covered with the PEI layer. This is because the PEI layer is not defect-free, the

high-molecular-weight branched PEI has a large free volume, and the mobility of the PEI segments during the electropolymerization might expose the bottom Au surface. This direct interaction

would further enhance the adhesion. Furthermore, compared with the conditions of 30% relative humidity and 23 °C, the adhesion between the pPy layer and PEI-O2 Au remained twice as strong as

that between the pPy layer and bare Au at 10% relative humidity and 60 °C (Fig. S2). After delamination of the pPy layer from the PEI-O2 Au electrode, the Au surface and the delaminated

side of the pPy surface were observed by SEM. Figure 5(d,e) reveals that no appreciable pPy or PEI residues were left on the Au surface after delamination; the electrode side of the pPy

layer showed a smooth surface profile similar to that of the bare Au surface. These results confirm that the cohesion of the pPy layer is stronger than the interfacial adhesion between the

pPy layer and PEI-O2 Au. The PEI patches seen in Fig. 3 disappeared following the pPy delamination, indicating that the interaction between PEI and the pPy layers is stronger than that

between PEI and plasma-treated Au. The interatomic interactions between PEI and pPy might not be strong because both the electropolymerized pPy backbone and the adsorbed PEI are positively

charged11,22. Therefore, the good adhesion between PEI and pPy layers might be due to other reasons, one of which would be the physical entanglement between the two entities. The pPy chains

growing from the surface may be physically entangled with the high-molecular-weight branched PEI layer. The large free volume of PEI23 and some segments stretching out from the surface would

contribute to this physical interaction. Cyclic voltammetry was performed to determine the effects of the PEI layer on the electrochemical performance of the overlaying pPy layers. Figure 

6(a) shows that all the cyclic voltammograms (CVs) of the pPy layers exhibit two faradaic peaks, which are indicative of a redox reaction of IC and are consistent with previous reports11.

The CV corresponding to the pPy layer on a PEI-O2 Au electrode was almost identical to that of the pPy layer on the bare electrode, confirming that a thin PEI coating does not affect the

electroactivities of the pPy layer and its dopant. Electrochemical impedance microscopy was used to investigate the electrochemical properties at different time scales (or frequency). Figure

S3 shows the Bode plot of the pPy films on different Au electrodes. In the frequency range 1 to 105 Hz, the impedance of the pPy film on PEI-O2 Au was similar to that on a bare Au,

indicating that the electrochemical properties of the pPy film were not affected by the underlying PEI layer. This trend is in good agreement with the voltammograms shown in Fig. 6. The

impedance data also indicate that the electrical and ionic conductivities of the pPy films on bare Au and PEI-O2 Au are identical, which is in agreement with the conductivity data mentioned

earlier. This result is consistent with previous work, where a physisorbed layer of polypeptides had negligible effect on the electrode impedance24. A broader peak-to-peak separation and

lower charge storage capacity were observed only for the sample comprising the pPy layers deposited on a thick LPEI/PAA coating. Charge storage capacity per unit area (areal capacity,

mC/cm2) of the pPy layer increased with increasing thickness, regardless of the surface pretreatments (i.e., PEI coating, O2 treatment). Therefore, in terms of achieving high capacity, using

PEI-O2 Au electrodes is advantageous over using bare Au electrodes since thicker pPy layers can be fabricated on PEI-O2 Au electrodes. The maximum areal capacity of the pPy layer on the

PEI-O2 Au electrode was more than twice as large as that of the pPy layer on the bare Au electrode: 538 mC/cm2 for 21-μm thick pPy layers on the PEI-O2 Au vs. 220 mC/cm2 for 8-μm thick pPy

layers on the bare Au. This maximum capacity value of the pPy layer (i.e., 538 mC/cm2, 21 μm) is comparable with the high areal capacity electrodes with similar thicknesses: carbon nanotubes

(~300 mC/cm2, 18 μm) on a porous carbon paper, pPy nanotubes (625 mC/cm2, 30 μm), and reduced graphene oxide/pPy films (~300 mC/cm2, 18 μm)25,26,27. In terms of the areal energy and power

densities, the 21-μm thick pPy layer delivered 35 μWh/cm2 at 2.8 mW/cm2, which is comparable to the densities delivered by 18-μm reduced graphene oxide/pPy films: 60 μhWh/cm2 at 1 mW/cm2 28.

Figure 6(b) shows that, regardless of the presence of the PEI layer, the charge storage capacity of the pPy layers decreased by only 25% as the scan rate was increased from 10 mV/s to 1000 

mV/s, showing that the PEI layer does not affect the retention capability of the pPy layer. These results demonstrate that using a PEI layer is effective for enhancing not only the adhesion

but also the thickness-dependent performance of pPy electrodes. In general, pPy doped with anions such as IC swells with negative potential sweep due to the influx of cations/water into the

pPy matrix, and the degree of expansion increases as the potential becomes more negative29. The electrochemical cycle stability of pPy films is likely to be dependent on the applied

potential window. As shown in Fig. S5, 7-µm-thick pPy films on both bare and PEI-O2 Au retained most of the initial capacity (>94%) after 500 cycles when subjected a moderate potential

sweep from -0.2 to 0.3 V (vs. Ag/AgCl), demonstrating excellent electrochemical cycle stability. In this potential window, no delamination of the pPy films occurred on both surfaces.

However, under a more negative sweep from −0.7 to 0.3 V (vs. Ag/AgCl), the pPy films on the bare Au electrodes delaminated instantly at the first negative potential sweep, while those on the

PEI-O2 Au electrode were well attached on the surface (Fig. 7(a)). Consequently, the charge stored in the pPy film on bare Au electrodes was not accessible for the second cycle, as

indicated by the flat line in Fig. 7(b). In contrast, the electrochemical charge stored in the pPy film on the PEI-O2 Au electrode was not only accessible in the second cycle (red line in

Fig. 7(b)) but also in the subsequent 100 cycles. These results demonstrate that our proposed surface treatment is beneficial for preventing the delamination during electrochemical

processes, and therefore, is useful for realizing pPy films with good electrochemical cycle stability. CONCLUSION In summary, this study introduces a simple method for enhancing the

interfacial bonding between a pPy layer and the underlying electrode surface by introducing an adhesion-enhancing PEI layer. The PEI layer promoted the adhesion of the pPy layer by up to 250

 % via interfacial interactions with the Au surface and by surface entanglement/interactions with the pPy layer. Importantly, this adhesion-promoting layer did not affect the physical and

electrochemical performances of the overlaying pPy layer. Therefore, this strategy expands the range of the pPy layer thickness without delamination (e.g., from 9 to 23 μm at room

temperature and relative humidity of 40 %), which is essential for fabricating high-performance electrodes for electrochemical and actuator applications. The areal capacity of the pPy layer

was proportional to the thickness, and it reached up to ~530 mC/cm2. Moreover, the pPy layer did not delaminate from the surface when it was deposited on the PEI-coated Au electrode even at

more negative potentials, where the pPy layers on the untreated surface tended to peel off from the surface due to electrochemical swelling. We believe that our strategy can be easily

expanded to various combinations of CPs, dopants, and substrates for the development of stable, high-performance CP electrodes for energy devices and actuators. CHANGE HISTORY * _ 16 APRIL

2019 A correction to this article has been published and is linked from the HTML and PDF versions of this paper. The error has not been fixed in the paper. _ REFERENCES * D’Arcy, J. M. _et

al_. Vapor-phase polymerization of nanofibrillar poly(3,4-ethylenedioxythiophene) for supercapacitors. _ACS Nano_ 8, 1500–1510 (2014). Article  Google Scholar  * Okuzaki, H., Kuwabara, T.

& Kunugi, T. Theoretical study of sorption-induced bending of polypyrrole films. _J. Polym. Sci. Pol. Phys._ 36, 2237–2246 (1998). Article  ADS  CAS  Google Scholar  * Liu, Y., Gan, Q.,

Baig, S. & Smela, E. Improving PPy adhesion by surface roughening. _J. Phys. Chem. C_ 111, 11329–11338 (2007). Article  CAS  Google Scholar  * Horvath, B., Kawakita, J. & Chikyow, T.

Adhesion of silver/polypyrrole nanocomposite coating to a fluoropolymer substrate. _Appl. Surf. Sci._ 384, 492–496 (2016). Article  ADS  CAS  Google Scholar  * Lallemand, F. _et al_.

Electrochemical synthesis and characterization of N-substituted polypyrrole derivatives on nickel. _Electrochim. Acta_ 52, 4334–4341 (2007). Article  CAS  Google Scholar  * Smela, E.

Thiol-modified pyrrole monomers: 4. Electrochemical deposition of polypyrrole over 1-(2-thioethyl)pyrrole. _Langmuir_ 14, 2996–3002 (1998). Article  CAS  Google Scholar  * Kim, S., Jang, L.

K., Park, H. S. & Lee, J. Y. Electrochemical deposition of conductive and adhesive polypyrrole-dopamine films. _Sci. Rep._ 6, 30475 (2016). Article  ADS  Google Scholar  * Kroschwald, F.

_et al_. Gold nanoparticle layers from multi-step adsorption immobilised on a polymer surface during injection molding. _J. Appl. Polym. Sci_. 133 (2016). * Lee, Y. M. _et al_.

Spin-assembled layer-by-layer films of weakly charged polyelectrolyte multilayer. _J. Nanosci. Nanotechnol._ 9, 7467–7472 (2009). CAS  PubMed  Google Scholar  * Blau, A. Cell adhesion

promotion strategies for signal transduction enhancement in microelectrode array _in vitro_ electrophysiology: An introductory overview and critical discussion. _Curr. Opin. Colloid. In._

18, 481–492 (2013). Article  CAS  Google Scholar  * Song, H. K. & Palmore, G. T. R. Redox-active polypyrrole: Toward polymer-based batteries. _Adv. Mater._ 18, 1764–1768 (2006). Article

  CAS  Google Scholar  * Peng, H. Y., Devarajan, M., Lee, T. T. & Lacey, D. Investigation of oxygen followed by argon plasma treatment on LED chip bond pad for wire bond application.

_Solder. Surf. Mt Technol._ 27, 129–136 (2015). Article  Google Scholar  * Radnik, R., Mohr, C. & Claus, P. On the origin of binding energy shifts of core levels of supported gold

nanoparticles and dependence of pretreatment and material synthesis. _Phys. Chem. Chem. Phys._ 5, 172–177 (2003). Article  CAS  Google Scholar  * Yun, H. J., Hong, H., Lee, J. & Choi, C.

J. Chemical and structural properties of polyethyleneimine film coated on a SiO2 substrate in different concentrations. _Mater. Trans._ 55, 801–805 (2014). Article  CAS  Google Scholar  *

Vanzetti, L. _et al_. XPS analysis of genomic DNA adsorbed on PEI-modified surfaces. _Surf. Interface. Anal._ 48, 611–615 (2016). Article  CAS  Google Scholar  * Huang, T. F., Zhang, L.,

Chen, H. L. & Gao, C. J. Sol-gel fabrication of a non-laminated graphene oxide membrane for oil/water separation. _J. Mater. Chem. A_ 3, 19517–19524 (2015). Article  CAS  Google Scholar

  * Ron, H., Matlis, S. & Rubinstein, I. Self-assembled monolayers on oxidized metals. 2. Gold surface oxidative pretreatment, monolayer properties, and depression formation. _Langmuir_

14, 1116–1121 (1998). Article  CAS  Google Scholar  * Fu, J. H. _et al_. pH-Amplified exponential growth multilayers: A facile method to develop hierarchical micro- and nanostructured

surfaces. _Langmuir_ 25, 672–675 (2009). Article  CAS  Google Scholar  * Kaynak, A., Rintoul, L. & Graeme, A. Change of mechanical and electrical properties of polypyrrole films with

dopant concentration and oxidative aging. _Mater. Res. Bull._ 35, 813–824 (2000). Article  CAS  Google Scholar  * Sultana, I. _et al_. Indigo carmine (IC) doped polypyrrole (PPy) as a

free-standing polymer electrode for lithium secondary battery application. _Solid State Ionics_ 215, 29–35 (2012). Article  CAS  Google Scholar  * Kim, J. H. _et al_. Understanding

mechanical behavior and reliability of organic electronic materials. _MRS Bull_ 42, 115–123 (2017). Article  CAS  Google Scholar  * Suriyanarayanan, S., Lee, H. H., Liedberg, B., Aastrup, T.

& Nicholls, I. A. Protein-resistant hyperbranched polyethyleneimine brush surfaces. _J Colloid. Interface Sci._ 396, 307–315 (2013). Article  ADS  CAS  Google Scholar  * Harris, C. S.,

Ratner, M. A. & Shriver, D. F. Ionic conductivity in branched polyethylenimine-sodium trifluoromethanesulfonate complexes. Comparisons to analogous complexes made with linear

polyethylenimine. _Macromol._ 20, 1778–1781 (1986). Article  ADS  Google Scholar  * Kim, S. Y., Kim, K. M., Hoffman-Kim, D., Song, H. K. & Pamore, G. T. R. Quantitative control of neuron

adhesion at a neural interface using a conducting polymer composite with low electrical impedance. _ACS Appl. Mater. Interfaces_ 3, 16–21 (2011). Article  Google Scholar  * Abidian, M. R.,

Corey, J. M., Kipke, D. R. & Martin, D. C. Conducting-polymer nanotubes improve electrical properties, mechanical adhesion, neural attachment, and neurite outgrowth of neural electrodes.

_Small_ 6, 421–429 (2010). Article  CAS  Google Scholar  * Kim, S. Y. _et al_. Rapid fabrication of thick spray-layer-by-layer carbon nanotube electrodes for high power and energy devices.

_Energy Environ. Sci._ 6, 888–897 (2013). Article  CAS  Google Scholar  * Wang, Z. H. _et al_. Surface modified nanocellulose fibers yield conducting polymer-based flexible supercapacitors

with enhanced capacitances. _ACS Nano_ 9, 7563–7571 (2015). Article  CAS  Google Scholar  * Shu, K. W., Wang, C. Y., Zhao, C., Ge, Y. & Wallace, G. G. A Free-standing

graphene-polypyrrole hybrid paper via electropolymerization with an enhanced areal capacitance. _Electrochim. Acta_ 212, 561–571 (2016). Article  CAS  Google Scholar  * Sen, S. _et al_. _In

situ_ measurement of voltage-induced stress in conducting polymers with redox-active dopants. _ACS Appl. Mater. Interfaces_ 8, 24168–24176 (2016). Article  CAS  Google Scholar  Download

references ACKNOWLEDGEMENTS This research was supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education

(2017R1D1A1B03034716) and Ministry of Science and ICT (2016H1D5A1910726). AUTHOR INFORMATION AUTHORS AND AFFILIATIONS * School of Mechanical Engineering, Kyungpook National University,

Daegu, 702-701, Republic of Korea Kyung-Geun Kim & Sung Yeol Kim Authors * Kyung-Geun Kim View author publications You can also search for this author inPubMed Google Scholar * Sung Yeol

Kim View author publications You can also search for this author inPubMed Google Scholar CONTRIBUTIONS S.Y. developed the idea, supervised the overall experiments. K.-G. carried out the

experiments and characterization. All authors discussed the results and reviewed the manuscript. CORRESPONDING AUTHOR Correspondence to Sung Yeol Kim. ETHICS DECLARATIONS COMPETING INTERESTS

The authors declare no competing interests. ADDITIONAL INFORMATION PUBLISHER’S NOTE: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional

affiliations. SUPPLEMENTARY INFORMATION SUPPORTING INFORMATION RIGHTS AND PERMISSIONS OPEN ACCESS This article is licensed under a Creative Commons Attribution 4.0 International License,

which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link

to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless

indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or

exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/. Reprints

and permissions ABOUT THIS ARTICLE CITE THIS ARTICLE Kim, KG., Kim, S.Y. Increase in Interfacial Adhesion and Electrochemical Charge Storage Capacity of Polypyrrole on Au Electrodes Using

Polyethyleneimine. _Sci Rep_ 9, 2169 (2019). https://doi.org/10.1038/s41598-019-38615-6 Download citation * Received: 22 June 2018 * Accepted: 31 December 2018 * Published: 18 February 2019

* DOI: https://doi.org/10.1038/s41598-019-38615-6 SHARE THIS ARTICLE Anyone you share the following link with will be able to read this content: Get shareable link Sorry, a shareable link is

not currently available for this article. Copy to clipboard Provided by the Springer Nature SharedIt content-sharing initiative